YUCERA
ST
Weißer Zirkonoxidblock
Bending Strength
Transmittance
Sintering temperature
Produktspezifikationen
Indication
Krone
Onlay
Inlay
Anterior
2-5 unit Bridges
System
98mm
95mm
89mm
others
Thickness：12/14/16/18/20/22/25mm
Farbe
A1
A2
A3
A3.5
A1
B1
B2
B3
B4
C1
C2
C3
C4
D2
D3
D4
OM1
OM2
OM3
Designed for
Customization and Strength
Full Customization Freedom
The white zirconia base allows technicians complete control over staining and characterization.
High Mechanical Strength
Supports demanding restorations requiring long-term durability.
Broad Clinical Applications
Suitable for crowns, bridges, and multi-unit restorations.
Stable Milling Performance
Ensures smooth machining and precise restoration margins.
Complete Customization for Every Restoration
ST White Zirconia provides a neutral white base, allowing dental labs complete freedom to apply their own staining and characterization for fully personalized restorations.
Its high flexural strength supports crowns, bridges, and multi-unit restorations, ensuring durability without compromising aesthetics.
Ideal for anterior and posterior restorations, single crowns, full-contour bridges, or complex restorative cases.
Stable milling and sintering properties help labs achieve predictable, high-quality results with minimal adjustments.
Sintering Curve
ST White Sintering Curve (1-5)
Sintering step
Start Tem-perature
End Tem-perature
Time
Rate
Step 1
Step 2
Step 3
Step 4
Step 5
Step 6
800℃
natural cooling 20℃
/
/
ST White Multilayer Sintering Curve (7-10)
Sintering step
Start Tem-perature
End Tem-perature
Time
Rate
Step 1
Step 2
Step 3
Step 4
Step 5
Step 6
800℃
natural cooling 20℃
/
/
ST White Multilayer Sintering Curve (10-14)
Sintering step
Start Tem-perature
End Tem-perature
Time
Rate
Step 1
Step 2
Step 3
Step 4
Step 5
Step 6
800℃
natural cooling 20℃
/
/
Fall
Dank der hervorragenden ästhetischen Eigenschaften dieses Zirkonoxidblocks erzielen die fertigen Restaurationen ein äußerst natürliches und ansprechendes Aussehen, was von unseren Kunden sehr positiv aufgenommen wurde. Nachfolgend finden Sie einige Fallbeispiele.