尤克拉
3D 自然
Multilayer Zirconia block
Bending Strength
Transmittance
Sintering temperature
产品规格
Indication
王冠
镶嵌
注入
前部
贴面
系统
98mm
95mm
89mm
others
Thickness：12/14/16/18/20/22/25mm
颜色
A1
A2
A3
A3.5
A1
B1
B2
B3
B4
C1
C2
C3
C4
D2
D3
D4
OM1
OM2
OM3
Predictable Aesthetics
and Efficient Workflows for Modern Dental Labs
Natural Multi-Layer Gradient
Features smooth transitions in color and translucency, closely replicating natural tooth structure from cervical to incisal area.
Balanced Strength Distribution
Engineered flexural strength gradient ensures durability in posterior regions while maintaining aesthetics in anterior restorations.
High Translucency for Esthetics
Optimized translucency levels enhance depth and vitality, delivering natural-looking restorations without excessive characterization.
Wide Clinical Indications
Suitable for veneers, crowns, inlays, bridges, and full-contour restorations, covering a broad range of clinical applications.
Designed for Everyday Aesthetic Excellence
11 gradual color transitions replicate the natural variation from cervical to incisal areas for realistic restorations.
A translucency gradient from 43% to 57% creates natural brightness and depth, closely resembling natural enamel.
Six precisely engineered layers eliminate visible boundaries and ensure smooth aesthetic transitions.
Strength gradually increases from ≥700 MPa to ≥1050 MPa while maintaining natural translucency.
The integrated gradient design delivers predictable shade matching and uniform results across every case.
Sintering Curve
3D Natural Multilayer Sintering Curve (1-5)
Sintering step
Start Tem-perature
End Tem-perature
Time
Rate
Step 1
Step 2
Step 3
Step 4
Step 5
Step 6
800℃
natural cooling 20℃
/
/
3D Natural Multilayer Sintering Curve (7-10)
Sintering step
Start Tem-perature
End Tem-perature
Time
Rate
Step 1
Step 2
Step 3
Step 4
Step 5
Step 6
800℃
natural cooling 20℃
/
/
案件
由于这种氧化锆瓷块具有优异的美学性能，最终修复体呈现出高度自然美观的外观，并获得了客户的积极反馈。以下是我们的一些案例图片。.